Utilization of Industrial Flour Waste as Biobriquette Adhesive: Application on Pyrolysis Biobriquette Sawdust Red Teak Wood

Harini Wahyuni , Andi Aladin , Ruslan Kalla , Muhammad Nouman , Ardimas Ardimas , MD. Shahariar Chowdhury

Abstract


Biobriquette is one of the alternative fuels derived from biomass. The biomass used in this research is red teakwood charcoal. This research purposes to utilize red teakwood charcoal as alternative fuels and then to knows best characters compressive strength, ignition power and caloric value according to Indonesian quality standards (SNI 01-6235-2000). Characteristics of biobriquettes are known by test ash content, moisture content, volatile matter, fix carbon, compressive strength, ignition power and caloric value. The materials used are red teakwood plus industrial flour waste. The process of making biobriquette begins with drying the material, pyrolysis during 150 minutes at a temperature of 400 oC, sieved with 40 mesh. The briquetting was using a cube-shaped mold with manual pressure which was then dried in an oven to a constant weight and tested its characteristics by the ASTM (American standard Testing and material) method. The results showed that the added adhesive was very take effect in producing the best briquettes. The characteristics of briquettes with the best optimum adhesive composition produce is adhesive 5% charcoal 95% produce ash content 5.49% , moisture content 4.26 %, volatile matter 26.89 %, fix carbon 63.12%, compressive strength 3.64 kgf/cm2, caloric value 7038 kcal/kg, and ignition power 0.03 gram/minute categorized as passing the specifications for the quality requirements briquettes of SNI 01-6235-2000.

Keywords


Biobriquette; Rred teakwood charcoal; Iindustrial flour waste; Compressive strength; Ignition power; Calorific value

Full Text:

PDF

References


Adhani, L., Masrya. M.A., Octavia, S.I and Sindiany, I.I. (2019), Analisis Bahan Bakar Alternatif Komposit Biobriket dari Enceng Gondok dengan Perekat Kotoran Sapi, Jurnal Al-Kimiya, 6(2): 81-86.

Ajimotokan, H.A., Ehindero, A.O., Ajao, K.A., Adeleke, A.A., Ikubanni, P.P and Babata, S.Y.L. (2019). Combustion Characteristics of Fuel Briquettes Made from Charcoal Particles and Sawdust Agglomerates, Science Direct, E00202.

Aladin, A and Dea, M. (2011). Sumber Daya Alam BatuBara, CV. Lubuk Agung: Bandung.

Aladin, A., Alwi, R.S and Syarif T. (2017). Design of Pyrolysis Reactor For Production of Bio-Oil And Bio-Char Simultaneously, International Seminar On Fundamental And Application Of Chemical Engineering, AIP Conf. Proc. 1840, 110010-1–110010-4.

Alfianolita, Y. (2018). Perbadingan Variasi Perekat pada Pembuatan Briket Tempurung Kelapa (Studi Kasus: Kecamatan Sutera Kabupaten Pesisir Selatan), Sekolah Tinggi Teknologi Industri (STTIND) Padang.

Anggoro, D.D., Hanif, M.D.W and Fathoni, M.Z., (2017). Pembuatan Briket Arang dari Campuran Tempurung Kelapa dan Serbuk Gergaji Kayu Sengon, Jurnal Teknik, 38(2): 1-5.

Anizar, H., Sribudiani, E and Somadona, S. (2020). Pengaruh Bahan Perekat Tapioka Dan Sagu Terhadap Kualitas Briket Arang Kulit Buah Nipah, Jurnal Perennial, 16(1): 11-17.

Ansar, Setiawati, D.A., Murad and Mliani, B.S. (2020). Karakteristik Fisik Briket Tempurung Kelapa menggunakan Perekat Tepung Tapioka, Jurnal Teknologi Pertanian, 13(1): 1-7.

Arake, S.R. (2017). Uji Kalor Briket Limbah Tongkol Jagung dan Sekam Padi dengan Proses Karbonisasi. Universitas Hasanuddin.

Ayuningtyas, E and Aridito, M.N. (2019). Studi Karakteristik Proses Pirolisis dan Arang dari Briket Serbuk Kayu dengan Variasi Laju Pemanasan Menggunakan Metode Pirolisis Single Rocket Stove, Jurnal Rekayasa Lingkungan, 19(1):1-14.

Faui, M.A., Mahfudz., Pudjiono, S., Hamdan, A.A., Hasna, T.M., Wibowo, A., Setiadi D and Rimbawanto, A. (2020). Beberapa Jenis Jati (Tectona sp.) Variasi dan Potensi Pemuliaannya, Badan Litbang dan Inovasi Lingkungan Hidup dan Kehutanan, Yogyakarta.

Febrianti, N., Filiana, F and Hasana P. (2020). Potensi Sumber Energi Terbarukan dari Biomassa yang Berasal dari Sumber Daya Alam di Balikpapan, Jurnal Presipitasi, 17(3): 316-323).

Handoko, R., Fadelan., and Malyadi, M. (2019). Analisa Kalor Bakar Briket, Berbahan Arang Kayu Jati, Kayu Asam, Kayu Johar, Tempurung Kelapa, dan Campuran, Jurnal Ilmiah Mahasiswa Komputek, 3(1), 14-21.

Haryanto, A., Hidayat, W., Hasanudin, U., Iryani, D.A., Kim, S., Lee, S., Yoo, J. (2021). Valorization of Indonesian Wood Wastes through Pyrolysis: A Review. Energies 2021, 14, 1407.

Jain, H., Vijayalakshmi, Y and Neeraja, T. (2018). Preparation of Biobriquettes Using Biomass Combinations and Estimation of its Caloric Value, International Journal of Sciences and Research (IJSR), 4(3): 322-324.

Kasman, Sudirman, I and Ulum, M.S. (2021). Karakterisasi Sifat Fisik Biobriket Campuran Batubara Buol., Arang Tempurung Kelapa dan Tongkol Jagung, Jurnal Gravitasi, 15(1): 1-9.

Kaulan, (2010). Proses Pengolahan dan Kontrol Proses Pengolahan Tepung Terigu Spesial, https://digilib.uns.ac.id/dokumen/download/15110/MzAwMDk=/Laporan-magang-di-PT-Indofood-Sukses-Makmur-Bogasari-flour-mills, accessed on July 31, 2021 at 21.30.

Kumar, G.S., Rao, C.J and Madhavi,S.K. (2016). Evaluation of Caloric Value of Bio-Briquette, International Journal of Research in Engineering and Technology, 5(9), 123-128.

Mandey, L.C., and Tarore, D. (2015). Pengembangan Produksi Biobriket dari Limbah Hasil Pertanian Sebagai Bahan Bakar Pengganti Minyak Tanah dan Gas, Jurnal Ilmu dan Teknologi Pakan, 3(2): 1-7.

Muhlis, A.M., Sahara and Fuadi, N. (2019). Uji Kualitas Biobriket Campuran Tempurung Kelapa, Tongkol Jagung dan Sekam Padi dengan Tepung Sagu sebagai Perekat, JFT, 6(1): 16–25.

Ningsih, E., Mirzayanti, Y.W., Himawan, H.S and Indriani, H.M. (2016). Pengaruh Jenis Perekat pada briket dari kulit Bintaro Terhadap Waktu Bakar, Prosidising Seminar Nasional Teknik Kimia “Kejuanganâ€, ISSN 1693-4393.

Nuhardin, I. (2018). Kualitas Limbah Serbuk Gergaji untuk Arang yang Diperoleh dengan Metode Pirolisi Lambat, Jurnal Tek. Mesin Univ. Muhammadiyah Metro, 2(2):166-173.

Parinduri, L and Parinduri, T. (2020). Konversi Biomassa Sebagai Sumber Energi Terbarukan, Journal of Electrial Technology, 5(2): 88-92.

Putri, R. E and Andasuryani. (2017). Studi mutu briket arang baku limbah biomassa, Jurnal teknologi pertanian andalas, 21(2): 143-151.

Qistina, I., Sukandar, D and Trilaksono. (2016). Kajian Kualitas Briket Biomassa dari Sekam Padi dan Tempurung Kelapa, Jurnal Kimia Valensi, 2: 136–142.

Rahmadani., Faizah, H., Farida, H, and Hamzah. (2017). Pembuatan Briket Arang Daun Kelapa Sawit (Elaeis guineensis Jacq.) Dengan Perekat Pati Sagu (Metroxylon sago Rott.), Jom Faperta, 4(1): 1-11.

Ristianingsih, Y., Ulfa, A and Syafitri, R.KS. (2017). Pengaruh suhu dan konsentrasi perekat terhadap karakteristik briket bioarang berbahan baku tandan kosong kelapa sawit dengan proses pirolisis, Jurnal konversi, 4(2): 16-22.

Salim Rais. (2016). Karakteristik dan Mutu Arang Kayu jati (Tectona grandis) dengan Sistem Pengarangan Campuran pada Metode Tungku Drum, Jurnal Riset Industri Hasil Hutan, 8(2):53-64.

Suharyati., Sadmoko, H.P., Jamaluddin, L.W and Nurian, I.P. (2019). Outlook Energi Indonesia, Sekretariat Jendral Dewan Energi Nasional, ISSN: 2527 3000.

Sulistyaningkarti, L and Utami, B. (2017). Pembuatan Briket Arang dari Limbah Organik Tongkol Jagung dengan Menggunakan Variasi Jenis dan Persentase Perekat, Jurnal Kimia dan Pendidikan Kimia, 2(1): 43-53.

Triantoro, A., Mustofa,A. and Daniah, M.H. (2020). Studi Karakteristik dan Kualitas Biobriket Campuran Bottom Ash Batubara dengan Arang Tempurung Kelapa, GEOSAPTA, 6(1): 13–17.

Usman, N.M. (2020). Mutu Briket Arang Kulit Buah Kakao Dengan Menggunakan Kanji Sebagai Perekat, Jurnal Perennial, 3(2): 55-58.

Western Cape Milling. (2021). Industrial Flour, http://wcmilling.co.za/product/industrial-flour/, accessed on August 01, 2021 at 17.00.

Yudanto and Kusumaningrum. (2017). Pembuatan Briket Bioarang dari Arang Serbuk Gergaji Kayu Jati, Repisotory Jurusan Teknik Kimia, Fakultas Teknik, Universitas Dipanegoro.




DOI: https://doi.org/10.58524/ijhes.v1i2.74

Refbacks

  • There are currently no refbacks.


 

Creative Commons License

International Journal of Hydrological and Environmental for Sustainability is licensed under a Creative Commons Attribution-ShareAlike 4.0 International LicensePublished by Foundation of Advanced Education (FoundAE). ISSN Numbers : p-ISSN 2828-6405 | e-ISSN 2828-5050